Before curing |
Performance index |
Reference standards |
5529 |
Appearance |
Visualization |
Translucent paste |
|
Relative Density(g/cm3) |
GB/T 533-2008 |
1.12 |
|
Surface drying time (min) Winter (November April) |
GB/T13477.5-2002 |
5~15 |
|
Surface drying time (min) Summer (May October) |
GB/T13477.5-2002 |
3~10 |
|
Complete curing time (H) |
Actual measurement of usage environment |
24H |
|
Curing type |
Actual measurement using the system |
Oxime Type |
|
Curing After |
Hardness(Shore A) |
GB/T 531.1-2008 |
30±5 |
Tensile strength(MPa) |
GB/T528-2009 |
2.0 |
|
Shear strength(MPa) |
GB/T7124-2008 |
2.0±0.2 |
|
Elongation at break(%) |
GB/T 528-2009 |
300 |
|
Peel Strength(N/mm) |
GB/T7124-2008 |
>30 |
|
Operating temperature range(℃) |
Actual measurement of usage environment |
-60~260 |
|
Volume resistivity (Ω·cm) |
GB/T 1692-2008 |
≥4.0×1014 |
|
Dielectric strength (kV/·mm) |
GB/T 1695-2005 |
≥18 |
|
Dielectric constant (1.2MHz) |
GB/T1693-2007 |
2.9 |